Инд. авторы:	Moskvichev V.V., Sukhodoeva N.V., Fedorova E.N., Popov A.S.
Заглавие:	Adhesion Energy in the Metal/Oxide System for the Case of High-Temperature Oxidation of Nickel-Based Superalloys
Библ. ссылка:	Moskvichev V.V., Sukhodoeva N.V., Fedorova E.N., Popov A.S. Adhesion Energy in the Metal/Oxide System for the Case of High-Temperature Oxidation of Nickel-Based Superalloys // Russian Metallurgy (Metally). - 2017. - Iss. 10. - P.884-889. - ISSN 0036-0295. - EISSN 1531-8648.
Внешние системы:	DOI: 10.1134/S0036029517100135; SCOPUS: 2-s2.0-85040995625; WoS: 000423266900020;
Реферат:	eng: The microstructure of the oxide layer is studied and the adhesion energy of the metal/oxide interface is determined after high-temperature isothermal oxidation (T = 1150 degrees C) of a single-crystal commercial Rene N5 nickel alloy. Experiments upon heating and rapid cooling are performed to initiate failure of the oxide layer. The elastic energy of the metal/oxide interface is determined using the model of circular buckling followed by edge delamination. Calculations are conducted for a homogeneous alumina layer and with allowance for the multilayer structure that forms at the initial stages of alloy oxidation. The adhesion energy is 72 and 27 J/m(2) for these cases, respectively.
Ключевые слова:	CRACKING; THICKNESS; ADHERENCE; SCALE; GROWTH; SPALLATION; COOLING RATE; SPALLING FAILURE; EB-PVD TBCS; THERMAL BARRIER COATINGS; adhesion energy; microstructure; oxide layer; nickel-based superalloy; high-temperature oxidation;
Издано:	2017
Физ. характеристика:	с.884-889