Инд. авторы:	Pavlov M.V., Pavlov I.V., Lineitsev A.V., Pavlov V.F.
Заглавие:	Glass Ceramic Materials Based on Beneficiation Tailings of Lead-Zinc Ore
Библ. ссылка:	Pavlov M.V., Pavlov I.V., Lineitsev A.V., Pavlov V.F. Glass Ceramic Materials Based on Beneficiation Tailings of Lead-Zinc Ore // Glass and Ceramics. - 2017. - Vol.73. - Iss. 11-12. - P.459-464. - ISSN 0361-7610. - EISSN 1573-8515.
Внешние системы:	DOI: 10.1007/s10717-017-9911-6; WoS: 000399148100016;
Реферат:	eng: A glass ceramic material was obtained from the beneficiation tailings of lead-zinc ores. The strength of the control samples was 22.26 MPa in bending and 90.22 MPa in compression. After 100 cycles of testing the samples for frost resistance, these characteristics changed to 9.61 MPa in bending and 35.30 MPa in compression.
Ключевые слова:	amorphous state; K-feldspar; frost resistance; strength; glass-ceramic material;
Издано:	2017
Физ. характеристика:	с.459-464