Заглавие:	Refractive index and compressibility of the KAlSi3O8 glass at pressures up to 6.0 GPa
Библ. ссылка:	Kuryaeva R.G. Refractive index and compressibility of the KAlSi3O8 glass at pressures up to 6.0 GPa // Glass Physics and Chemistry. - 2011. - Vol.37. - Iss. 3. - P.243-251. - ISSN 1087-6596. - EISSN 1608-313X.
Внешние системы:	DOI: 10.1134/S1087659611030060; SCOPUS: 2-s2.0-80052680187;
Реферат:	eng: The refractive index of potassium aluminosilicate glass of the KAlSi 3O8 composition in the pressure range up to 6.0 GPa has been measured using a polarizing interference microscope and an apparatus with diamond anvils. The changes in the relative density, which characterize the compressibility of the K2O · Al2O3 · 6SiO2 glass, have been estimated in the pressure range under investigation from the measured refractive indices within the framework of the theory of photoelasticity. The results have been compared with the data previously obtained for the Na2O · Al2O3 · 6SiO2 glass. Although the molar contents of Al 2O3 and M2O (where M = K or Na) are identical in these glasses, the KAlSi3O8 glass exhibits a higher compressibility, which agrees with the lower degree of depolymerization of this glass as compared to that observed in the NaAlSi3O8 glass. The pressure derivative of the bulk modulus , which is calculated from the Birch-Murnaghan equation for the KAlSi3O8 glass (K' t = 7-9), is higher than that for the NaAlSi3O8 glass (K't = 5.5-6.0). An increase in the pressure derivative of the bulk modulus K't upon replacement of the Na+ cations by the K+ cations is explained by the inhibition of compression of the large K+ cations, which are located in cavities and have a considerably larger orbital radius than the Na+ cations. This manifests itself in the fact that the curves describing the dependences of the change in the relative density (d - d0)/d (compressibility) on the pressure P for the KAlSi3O8 and NaAlSi3O 8 glasses converge at pressures above 4.0 GPa. © Pleiades Publishing, Ltd., 2011.
Ключевые слова:	Refractive index and compressibility in the pressure range up to 6.0 GPa; Aluminosilicate glass; Birch-Murnaghan equation; Degree of depolymerization; Diamond anvil; KAlSi3O8 glass; Molar content; Polarizing interference microscope; Pressure derivatives; Pressure ranges; KAlSi3O8 glass; Glass; Silicon compounds; Refractometers; Refractive index; Positive ions; Light refraction; Elastic moduli; Compressibility; Aluminum; Aluminosilicates; Relative density;
Издано:	2011
Физ. характеристика:	с.243-251