Инд. авторы:	Nadolinny V., Komarovskikh A., Palyanov Y., Borzdov Y., Kupriyanov I., Rakhmanova M., Yuryeva O.
Заглавие:	Silicon-containing defects in HPHT diamond synthetized in Mg-Si-C system
Библ. ссылка:	Nadolinny V., Komarovskikh A., Palyanov Y., Borzdov Y., Kupriyanov I., Rakhmanova M., Yuryeva O. Silicon-containing defects in HPHT diamond synthetized in Mg-Si-C system // Physica Status Solidi. A - Applications and Materials Science. - 2015. - Vol.212. - Iss. 11. - P.2460-2462. - ISSN 1862-6300. - EISSN 1862-6319.
Внешние системы:	DOI: 10.1002/pssa.201532165; РИНЦ: 26762211; SCOPUS: 2-s2.0-84929447965; WoS: 000366588100012;
Реферат:	eng: Diamond crystals synthesized in the Mg-Si-C system at high pressure high temperature (HPHT) conditions have been studied by EPR and photoluminescence. In the EPR spectra of the samples, two centers with S = 1 and S = 1/2 were detected along with substitutional nitrogen P1. Investigation of the angular dependence allowed us to establish spin Hamiltonian parameters of these centers, which turned out to be silicon containing centers KUL1 and KUL8, neutral and negatively charged silicon atom in a split-vacancy configuration, respectively. In the photoluminescence spectra of the diamond crystals there was an intense line at 737 nm corresponding to the (Si-V) - defect. X-ray irradiation, as well as UV excitation, led to an increase in relative intensities of P1 and KUL1 EPR signals, at the same time relative intensity of KUL8 decreased. Heat treatment at 773K led to the recovery of the initial EPR spectrum. Our results confirm the hypothesis that KUL8 center is negatively charged state of Si-V defect. (C) 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Ключевые слова:	RESONANCE; FILMS; CVD DIAMOND; GROWTH; electron paramagnetic resonances; diamond; defects; silicon; CENTERS;
Издано:	2015
Физ. характеристика:	с.2460-2462